This paper presents an extensive experimental campaign over the effect of SiC concentration on the aero-thermal behavior of ultra-high temperature ceramics in the hypersonic atmospheric re-entry environment. Four compositions made of ZrB2 with different amount of SiC from 5 to 18 vol.% were exposed to the supersonic plasma flow of an arc-heated plasma wind tunnel, at specific total enthalpies up to 20 MJ/kg, measuring their surface temperature by non-intrusive diagnostic equipment, including two-color pyrometers and an infrared thermo-camera. As SiC content increases, maximum steady-state temperature reached on the surface decreased and emissivity value are higher. During some tests, a spontaneous temperature jump in the order of 400 K was observed, which only occurred on the front surface of the sample. Surface temperatures over 2800 K were measured after a temperature jump. The composition which experienced the jump showed an external surface reaction made of only zirconia layer on the front surface, probably appearing upon complete removal of liquid borosilicate glass which forms during exposure to oxygen and is still present on the surface of samples with higher SiC content. The experiments demonstrated that the temperature jump, closely related to the overall thermal stability of the material, appears favoured by lower SiC amount, but it can be triggered also in case of larger SiC content (up to at least 15% vol.), as long as the flow total enthalpy and the exposure time are sufficiently high.

Effect of SiC concentration on aero-thermal behavior of ZrB2-based ceramics in hypersonic environment

Savino Raffaele
Penultimo
Writing – Review & Editing
;
Monteverde F
Ultimo
Writing – Review & Editing
2019

Abstract

This paper presents an extensive experimental campaign over the effect of SiC concentration on the aero-thermal behavior of ultra-high temperature ceramics in the hypersonic atmospheric re-entry environment. Four compositions made of ZrB2 with different amount of SiC from 5 to 18 vol.% were exposed to the supersonic plasma flow of an arc-heated plasma wind tunnel, at specific total enthalpies up to 20 MJ/kg, measuring their surface temperature by non-intrusive diagnostic equipment, including two-color pyrometers and an infrared thermo-camera. As SiC content increases, maximum steady-state temperature reached on the surface decreased and emissivity value are higher. During some tests, a spontaneous temperature jump in the order of 400 K was observed, which only occurred on the front surface of the sample. Surface temperatures over 2800 K were measured after a temperature jump. The composition which experienced the jump showed an external surface reaction made of only zirconia layer on the front surface, probably appearing upon complete removal of liquid borosilicate glass which forms during exposure to oxygen and is still present on the surface of samples with higher SiC content. The experiments demonstrated that the temperature jump, closely related to the overall thermal stability of the material, appears favoured by lower SiC amount, but it can be triggered also in case of larger SiC content (up to at least 15% vol.), as long as the flow total enthalpy and the exposure time are sufficiently high.
2019
Istituto di Scienza, Tecnologia e Sostenibilità per lo Sviluppo dei Materiali Ceramici - ISSMC (ex ISTEC)
Arc-jet wind tunnel test
SiC
Temperature jump
Ultra-high temperature ceramics
ZrB2
File in questo prodotto:
File Dimensione Formato  
IAC-19-C2.4.4.x50232_Mungiguerra.pdf

solo utenti autorizzati

Tipologia: Versione Editoriale (PDF)
Licenza: NON PUBBLICO - Accesso privato/ristretto
Dimensione 1.01 MB
Formato Adobe PDF
1.01 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.14243/396433
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 0
  • ???jsp.display-item.citation.isi??? ND
social impact