The thermal and mechanical properties of biocomposites of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) containing 5 wt % of valerate units, with 20 wt % of potato pulp powder were investigated in order (i) to obtain information on possible miscibility/compatibility between the biopolymers and the potato pulp, and (ii) to quantify how the addition of this filler modifies the properties of the polymeric material. The potato pulp powder utilized is a residue of processing for the production and extraction of starch. The final aim of this study is the preparation of PHBV based materials with reduced cost, thanks to biomass valorization, in agreement with the circular economy policy, as result of the incorporation of agricultural organic waste. The results showed that the potato pulp powder does not act as reinforcement, but rather as filler for the PHBV polymeric matrix. A moderate loss in mechanical properties is detected (decrease in elastic modulus, tensile strength and elongation at break), which regardless still meets the technical requirements indicated for rigid packaging production. In order to improve the mechanical response of the PHBV/potato pulp powder biocomposites, surface treatment of the potato pulp powder with bio-based and petroleum-based waxes was investigated. Good enhancement of the mechanical properties was achieved with the natural carnauba and bee waxes.

The thermal, mechanical, and rheological properties of biocomposites of poly(lactic acid) (PLA) with potato pulp powder were investigated in order to (1) quantify how the addition of this filler modifies the structure of the polymeric material and (2) to obtain information on the possible miscibility and compatibility between PLA and the potato pulp. The potato pulp powder utilized is a residue of the processing for the production and extraction of starch. The study was conducted by analyzing the effect of the potato pulp concentration on the thermal, mechanical, and rheological properties of the biocomposites. The results showed that the potato pulp powder does not act as reinforcement but as filler for the PLA polymeric matrix. A progressive decrease in elastic modulus, tensile strength, and elongation at break was observed with increasing the potato pulp percentage. This moderate loss of mechanical properties, however, still meets the technical requirements indicated for the production of rigid packaging items. The incorporation of potato pulp powder to PLA offers the possibility to reduce the cost of the final products and promotes a circular economy approach for the valorization of agro-food waste biomass.